Shrinkage is a crucial property of plastics, directly impacting product molding. In plastic injection mold и литьё под давлением industries, designers must grasp shrinkage, as it influences mold design.

For product designers, while not directly manufacturing plastic items, understanding shrinkage is vital. Otherwise, their designs might cause unnecessary issues during production, especially with thicker-walled products.

This article comprehensively explores plastic shrinkage, offering insights for both mold and product designers.

What is Plastic Shrinkage?

Plastic shrinkage refers to the percentage decrease in dimensions from the initial, uncooled size to the cooled, room temperature size. It’s not only due to thermal expansion and contraction but also related to various molding factors, hence termed molding shrinkage.

Specifically, shrinkage can be calculated using this formula:

Shrinkage = (Original size – Cooled size) / Original size × 100%

The extent of plastic shrinkage depends on factors such as material type, composition, moisture absorption, and mold temperature. For instance, crystalline plastics typically exhibit greater shrinkage than amorphous plastics.

The Impact of Shrinkage on Parts

Shrinkage affects parts in multiple ways, including product performance, appearance, and production costs.

Firstly, it diminishes part dimensional accuracy. Improperly controlled shrinkage rates can deviate part dimensions from design specifications, affecting assembly precision and fitting performance. In the automotive industry, for example, shrinkage can hinder the smooth operation of components like doors and windows, impacting overall vehicle performance and safety.

Secondly, it influences part appearance quality. As plastic parts usually have smooth surfaces, shrinkage can cause surface irregularities, diminishing product aesthetics and texture. This not only affects consumer purchasing decisions but also tarnishes a company’s brand image.

Moreover, shrinkage increases production costs. To control shrinkage rates, injection molding companies must take various measures, such as adjusting mold designs and optimizing injection molding processes. These measures require significant human and material resources, escalating production costs. Additionally, due to decreased part dimensional accuracy, companies may need secondary processing or repairs, further increasing production and time costs.

Why Product Designers Need to Know Injection Molding Shrinkage

Although injection molding factories resolve shrinkage issues during production, product designers still need to grasp shrinkage-related knowledge. Here’s why:

Optimizing designs: Understanding shrinkage allows designers to anticipate size changes during production, optimizing designs for precise, consistent results.

Material selection: Different plastics exhibit varying shrinkage levels during molding. Knowledge of shrinkage aids in selecting suitable materials based on design requirements.

Iterative design process: Anticipating and addressing shrinkage issues early shortens development cycles, expediting product launches.

Cost efficiency: Minimizing shrinkage-related problems reduces waste, rework, and delays, enhancing cost efficiency in production processes. Designers aware of shrinkage can create economically viable products.

Factors Influencing Injection Molding Shrinkage

Shrinkage rates vary among plastics due to factors like thickness, molding processes, and environmental conditions. For product designers, it’s crucial to note that:

  1. Thicker walls lead to longer cooling times and greater shrinkage.
  2. Features like reinforcements and engravings resist shrinkage, resulting in smaller shrinkage rates in these areas.

For mold designers, attention should be paid to how plastic shrinkage is affected, primarily in:

Molding Processes Factor

  • Consistent molding temperature reduces shrinkage.
  • Increased injection pressure decreases shrinkage.
  • Higher melt temperature reduces shrinkage.
  • Higher mold temperature increases shrinkage.
  • Prolonged pressure maintains shrinkage reduction.
  • Longer cooling time within the mold decreases shrinkage.
  • High injection speeds slightly increase shrinkage.
  • Initial shrinkage is large, stabilizing after approximately two days.

Plastic Structure Factor

  • Thick-walled parts exhibit higher shrinkage rates.
  • Parts with inserts have lower shrinkage rates.
  • Complex shapes have smaller shrinkage rates.
  • Shrinkage is typically smaller in the flow direction.
  • Elongated parts show lower shrinkage along the length.
  • Shrinkage along the length is smaller than thickness.

Mold Structure Factor

  • Larger gate size reduces shrinkage.
  • Parts farther from the gate have smaller shrinkage.
  • Restricted parts of the mold exhibit less shrinkage.

Plastic Properties Factor

  • Crystalline plastics exhibit greater shrinkage than amorphous ones.
  • Plastics with good flowability have smaller molding shrinkage.
  • Adding fillers to plastics significantly reduces shrinkage.
  • Different batches of the same plastic exhibit varying shrinkage rates.

Various materials exhibit different shrinkage in injection molding

Due to the multitude of factors influencing plastic shrinkage rates, the values exhibit a considerable range of fluctuation. For instance, the shrinkage rate of ABS you might find online could be approximately 0.4% to 0.7%. To provide a more precise range, FirstMold has compiled several detailed tables of plastic shrinkage rates.

PA6 Plastic Shrinkage:

Material and DescriptionMolding Shrinkage (%)Remarks
15% Glass Fiber Reinforced PA60.5-0.8PA6G15
20% Glass Fiber Reinforced PA60.4-0.6PA6G20
30% Glass Fiber Reinforced PA60.3-0.5PA6G30
40% Glass Fiber Reinforced PA60.1-0.3PA6G40
50% Glass Fiber Reinforced PA60.1-0.3PA6G50
25% Glass Fiber Reinforced Flame Retardant PA60.2-0.4Z-PA6G25
30% Glass Fiber Reinforced Flame Retardant PA60.2-0.4Z-PA6G30
30% Glass Fiber Reinforced Halogen-Free Flame Retardant PA60.2-0.4Z-PA6G30
Halogen-Free Flame Retardant PA60.8-1.2Z-PA6
30% Mineral Filled Halogen-Free Flame Retardant PA60.5-0.8Z-PA6M30
30% Glass Microsphere Filled PA60.8-1.2PA6M30
30% Glass Fiber Mineral Composite Filled PA60.3-0.5PA6M30
40% Glass Fiber Mineral Composite Filled PA60.2-0.5PA6M40
30% Mineral Filled PA60.6-0.9PA6M30
40% Mineral Filled PA60.4-0.7PA6M40
General Injection Grade PA61.4-1.8PA6
Rapid Prototyping PA61.2-1.6PA6
General Toughened PA61.0-1.5PA6
Medium Toughened PA60.9-1.3PA6
Super Toughened PA60.9-1.3PA6
MoS2 Filled Wear-Resistant PA61.0-1.4PA6

PA6 Plastic Shrinkage:

Material and DescriptionMolding Shrinkage (%)Remarks
15% Glass Fiber Reinforced PA660.6-0.9PA66G15
20% Glass Fiber Reinforced PA660.5-0.8PA66G20
25% Glass Fiber Reinforced Heat Resistant Oil PA660.4-0.7PA66G25
30% Glass Fiber Reinforced PA660.4-0.7PA66G30
30% Glass Fiber Reinforced Hydrolysis Resistant PA660.3-0.6PA66G30
40% Glass Fiber Reinforced PA660.2-0.5PA66G40
50% Glass Fiber Reinforced PA660.1-0.3PA66G50
25% Glass Fiber Reinforced Flame Retardant PA660.2-0.4Z-PA66G25
30% Glass Fiber Reinforced Flame Retardant PA660.2-0.4Z-PA66G30
30% Mineral Filled Halogen-Free Flame Retardant PA660.2-0.4PA66M30
Halogen-Free Flame Retardant PA660.8-1.2Z-PA66
30% Mineral Filled Halogen-Free Flame Retardant PA660.4-0.7Z-PA66M30
30% Glass Microsphere Filled PA660.8-1.2PA66M30
30% Glass Fiber Mineral Composite Filled PA660.2-0.5PA66M30
30% Mineral Filled PA660.6-0.9PA66M30
40% Mineral Filled PA660.4-0.7PA66M40
General Injection Grade PA661.5-1.8PA66
Rapid Prototyping PA661.5-1.8PA66
General Toughened PA661.2-1.7PA66
Medium Toughened PA661.2-1.6PA66
Super Toughened PA661.2-1.6PA66
MoS2 Filled Wear-Resistant PA661.2-1.6PA66

PP Plastic Shrinkage:

Material and DescriptionMolding Shrinkage (%)Remarks
20% Talc Filled PP1.0-1.5PPM20
30% Talc Filled PP0.8-1.2PPM30
40% Talc Filled PP0.8-1.0PPM40
20% Talc Filled Toughened PP1.0-1.2PPM20
20% Calcium Carbonate Filled PP1.2-1.6PPM20
10% Glass Fiber Reinforced PP0.7-1.0PPG10
20% Glass Fiber Reinforced PP0.5-0.8PPG20
30% Glass Fiber Reinforced PP0.4-0.7PPG30
20% Glass Microsphere Filled PP1.2-1.6PPM20
30% Glass Microsphere Filled PP1.0-1.2PPM20
Brominated Flame Retardant PP1.5-1.8PP
Halogen-Free Flame Retardant PP1.3-1.6PP
High Flow High Impact PP1.5-2.0PP
General Toughened PP1.5-2.0PP
Medium Toughened PP1.4-1.9PP
Super Toughened PP1.3-1.8PP
Heat Aging Resistant PP11.5-2.0PP1
Heat Aging Resistant PP21.5-2.0PP2
Heat Aging Resistant PP31.5-2.0PP3
Impact Resistance Weathering Resistance PP41.5-2.0PP4
High Impact Weathering Resistance PP51.5-1.8PP5
20% Talc Filled PP61.0-1.2PP6
30% Talc Filled PP70.9-1.1PP7
40% Talc Filled PP80.8-1.0PP8

PC Plastic Shrinkage:

Material and DescriptionMolding Shrinkage (%)Remarks
10% Glass Fiber Reinforced PC0.3-0.5PCG10
20% Glass Fiber Reinforced PC0.3-0.5PCG20
25% Glass Fiber Reinforced PC0.2-0.4PCG25
30% Glass Fiber Reinforced PC0.2-0.4PCG30
20% Glass Fiber Reinforced Flame Retardant PC0.2-0.4Z-PCG20
25% Glass Fiber Reinforced Flame Retardant PC0.2-0.4Z-PCG25
30% Glass Fiber Reinforced Flame Retardant PC0.2-0.4Z-PCG30
20% Glass Fiber Reinforced Halogen-Free Flame Retardant PC0.2-0.4Z-PCG20
30% Glass Fiber Reinforced Halogen-Free Flame Retardant PC0.1-0.3Z-PCG30
20% Glass Microsphere Filled PC0.3-0.6PCM20

PC/ABS Plastic Shrinkage:

Material and DescriptionMolding Shrinkage (%)Remarks
20% Glass Fiber Reinforced PC/ABS0.2-0.4PC/ABSG20
Brominated Flame Retardant PC/ABS0.3-0.6Z-PC/ABS
Halogen-Free Flame Retardant PC/ABS0.4-0.7Z-PC/ABS
Weathering Resistant PC/ABS0.4-0.7ПК/АБС
35% PC0.4-0.6ПК/АБС
65% PC0.4-0.7ПК/АБС
85% PC0.4-0.7ПК/АБС

PC/PBT Plastic Shrinkage:

Material and DescriptionMolding Shrinkage (%)Remarks
10% Glass Fiber Reinforced PC/PBT0.5-0.8PC/PBTG10
20% Glass Fiber Reinforced PC/PBT0.4-0.6PC/PBTG20
30% Glass Fiber Reinforced PC/PBT0.3-0.5PC/PBTG30
30% Glass Fiber Reinforced Flame Retardant High Heat Resistant PC/PBT0.3-0.5Z-PC/PBTG30
High Impact High Heat Resistant PC/PBT0.6-1.0ПК/ПБТ

ABS Plastic Shrinkage:

Here’s the table based on the provided information:

Material and DescriptionMolding Shrinkage (%)Remarks
20% Glass Fiber Reinforced ABS0.2-0.4ABSG20
25% Glass Fiber Reinforced ABS0.2-0.4ABSG25
30% Glass Fiber Reinforced ABS0.1-0.3ABSG30
20% Glass Fiber Reinforced Flame Retardant ABS0.1-0.3Z-ABSG20
General Flame Retardant Grade ABS0.4-0.7Z-ABS
General Injection Grade ABS0.4-0.7ABS
Weathering Resistant Grade ABS0.4-0.7ABS

How to Prevent Fluctuations in Plastic Shrinkage?

Measures to Adopt

Achieving Flow and Gate Balance

As the title mentioned, shrinkage rates vary due to resin pressure changes. In the case of single-cavity molds with multiple gates or multi-cavity molds, proper gating balancing is essential. Balancing the gates is necessary for uniform resin flow, which depends on the flow resistance within the runner. Hence, it’s preferable to achieve runner balance before gate balancing.

Mold Cavity Arrangement

To facilitate the setup of molding conditions, attention must be paid to mold cavity arrangement. Since the molten resin carries heat into the mold, under typical cavity arrangements, the mold temperature distribution forms concentric circles centered around the gate. Therefore, when selecting the arrangement of cavities in multi-cavity molds, it’s important to ensure both easy runner balance and a concentric arrangement centered around the gate.

Preventing Molding Deformation

Molding deformation occurs due to uneven shrinkage resulting in internal stress. To prevent uneven shrinkage, especially in cases like circular products with holes at the gear center, a gate must be placed at the center. However, when there’s a significant difference in shrinkage rates between the resin’s flow direction and the perpendicular direction, the disadvantage of forming an ellipse arises.

For higher roundness precision, it’s necessary to set up 3-point or 6-point gates. However, it’s crucial to ensure proper balancing of each gate. When using side gates, a 3-point gate may enlarge the inner diameter of cylindrical products. In situations where gate marks are not permissible on the surface and end faces, it’s advisable to minimize the use of internal side multi-point gates, which can yield favorable results.


Вам также может понравиться

Добавить комментарий

Ваш адрес email не будет опубликован. Обязательные поля помечены *